THE EFFECTS OF HEAT TREATMENT ON THE MECHANICAL PROPERTIES OF A WELDED JOINT OF MEDIUM CARBON STEEL

  • Type: Project
  • Department: Material Science
  • Project ID: MCI0009
  • Access Fee: ₦5,000 ($14)
  • Pages: 86 Pages
  • Format: Microsoft Word
  • Views: 828
  • Report This work

For more Info, call us on
+234 8130 686 500
or
+234 8093 423 853
ABSTRACT
The effect  of Heat treatment on the Mechanical Properties of a welded joint of medium carbon steel has been carried out.  The materials were cut, welded, to get 27 samples needed. Thereafter, Heat Treatment was carried out on the samples. Then the specimens were grouped into two groups, group A and group B. In group  A, after the heat treatment on the welded specimens, one sample was quenched in water immediately, another was oil-quenched and the third one was allowed to cool under still air. In group B, 25 specimens were heated to 9100C (Austenitic temperature) and were divided into two. Remaining one  in the furnace was removed and allowed to  cool under still air. 12 sample were quenched in water, tempered at different temperature as follows 2500c, 4500c, 6600c, and quenched at different time interval, 30,60,90, 120 and the same process was applied to the oil-quenched specimens. One was brought out from each specimen that were water-quenched and oil-quenched. Then the remaining one in the furnace was removed to cool under still air. From group A and group B, 6 Samples was prepared for testing. Hardness test and Microstructure test were carried out on the experimental specimens. The result showed that the hardness decreases as the temperature and time increases. The Microstructureal  test revealed that the structure of welded joint of medium carbon steel could be well refined by heat treatment. 




TABLE OF CONTENTS
Title page
Approval page
Dedication
Acknowledgment
Abstract
Table of contents
CHAPTER ONE
1.0  INTRODUCTION
1.1 Welding
1.1.1 Arc Welding Processes
1.1.2 Oxy Gas Welding Processes 
1.1.3 Structural Changes In Steel During Welding.
1.1.4 Welded Joint 
1.1.5 Types Of Welded Joints Are
1.1.6 Butt Welded Joint
1.1.7 Types Of Butt Welded Joints:
1.1.8 Corner Welded Joints
1.1.9 Edge Welded Joint
1.1.10 Lap Welded Joint
1.1.11 Tee Welded Joints
1.1.12 Method of Welding Tee Joint
1.1.14 Inclusions 
1.1.15 Cracking
1.1.16 Under Cut
1.1.17.Lamellar Tearing
1.2 Aims and Objectives Of This Project Work  


CHAPTER TWO
2.0 LITERATURE REVIEW
2.1steel                                                                                                                                                              2.1.1 Types Of Steel
2.1.2 Weldability
2.1.3 The Heat Treatment Of Steels   
2.1.4 Hardening Of Steel
2.1.5 Different Quenching Media
2.2 Tempering            
2.2.2 Annealing
2.3 Grain Size
2.4.1 Structure Changes In Steel During Heat Treatment
2.4.2 Testing Of Materials
2.5 Hardness Test
CHAPTER THREE
EXPERIMENTAL PROCEDURE
3.1    Sourcing of The Material
3.2 Preparation of the Materials For Welding
3.3 Welding of the Specimens
3.3.2 Weld Procedure
3.3 Heat Treatment Process
3.4 Heat Treatment Procedure
3.4.1 Hardness Testing
3.4.2 Hardness Procedure
3.5 Microstructrue Test.
3.5.1 Micro Graph Procedure
CHAPTER FOUR
4.0  MECHANICAL TEST
CHAPTER FIVE
CONCLUSIONS AND RECOMMENDATIONS
5.0     Conclusion
5.1 Recommendations
  References


LIST OF FIGURES
Figure 1:         Welded medium carbon steel
Figure 2.1:     Equilibrium Phase Diagram
Figure 2.2         Temperature –time transformation diagram
Figure 3.1:      Square steel bar






THE EFFECTS OF HEAT TREATMENT ON THE MECHANICAL PROPERTIES OF A WELDED JOINT OF MEDIUM CARBON STEEL
For more Info, call us on
+234 8130 686 500
or
+234 8093 423 853

Share This
  • Type: Project
  • Department: Material Science
  • Project ID: MCI0009
  • Access Fee: ₦5,000 ($14)
  • Pages: 86 Pages
  • Format: Microsoft Word
  • Views: 828

500
Leave a comment...

    Related Works

    ABSTRACT Steel is arguably the world’s most ‘advanced” material. It is a very versatile material with a wide range of attractive properties which can be produced at a very competitive cost. It has a diverse range of applications, and is second only to concrete in its annual production tonnage. Steel is not a new invention which leads to a... Continue Reading
    This project covers a study of the effect of seawater corrosion on 0.34% and 0.36% carbon steel  compositions. Two (2) specimens (steel rods) of length 150mm (each) for both steel compositions were  obtained. Out of each was gotten four (4) specimens of 10mm length, 10mm diameter and two  (2) specimens of 50mm length, 10mm diameter. This... Continue Reading
    This project covers a study of the effect of seawater corrosion on 0.34% and 0.36% carbon steel compositions. Two (2) specimens (steel rods) of length 150mm (each) for both steel compositions were obtained. Out of each was gotten four (4) specimens of 10mm length, 10mm diameter and two (2) specimens of 50mm length, 10mm diameter. This yielded a... Continue Reading
    Research and optimization of cooling of electronic components using heat sinks becomes increasingly important in modern industry. Numerical methods with experimental real world verification are the main tools to evaluate efficiency of heat sinks or heat sink systems. In this research, the physical problems associated with heat removal of... Continue Reading
    Research and optimization of cooling of electronic components using heat sinks becomes increasingly important in modern industry. Numerical methods with experimental real world verification are the main tools to evaluate efficiency of heat sinks or heat sink systems. In this research, the physical problems associated with heat removal of... Continue Reading
    By definition, penetrant testing (PT) is the resurgence of a liquid (or a gas) from a discontinuity in which it had previously been introduced during a penetration operation. A logical extension of the visual examination, this method makes it possible to detect discontinuities opened to the surface of the controlled part in the form of colored or... Continue Reading
    By definition, penetrant testing (PT) is the resurgence of a liquid (or a gas) from a discontinuity in which it had previously been introduced during a penetration operation. A logical extension of the visual examination, this method makes it possible to detect discontinuities opened to the surface of the controlled part in the form of colored or... Continue Reading
    Carbon steel corrosion is a commonly encountered issue in pipelines transporting hydrocarbons containing corrosive agents such as CO2, H2S and water. As a result, several corrosion prediction models have been put forward over the years although no standard model exists for corrosion prediction in the industry. Two of such models are the Norsok... Continue Reading
    Carbon steel corrosion is a commonly encountered issue in pipelines transporting hydrocarbons containing corrosive agents such as CO2, H2S and water. As a result, several corrosion prediction models have been put forward over the years although no standard model exists for corrosion prediction in the industry. Two of such models are the Norsok... Continue Reading
    ABSTRACT   Organizational justice is an essential component and predictor of successful organizations. Organization that is fair and just in its procedures, policies, interactions and distribution systems, employees of that organization give better response to the organization in terms of their positive behaviours and productivity thus the main... Continue Reading
    Call Us Get this work