Fracture Mechanics of Glass Fibre Reinforced Polyester Composites (Gfrp) Subjected to Impact Load

  • Type: Project
  • Department: Mechanical Engineering
  • Project ID: MCE0250
  • Access Fee: ₦5,000 ($14)
  • Pages: 85 Pages
  • Format: Microsoft Word
  • Views: 179
  • Report This work

For more Info, call us on
+234 8130 686 500
or
+234 8093 423 853

ABSTRACT

Glass mat reinforcement, which can be easily shattered, is widely used across the world in military, automobile, civil, railway and electronic engineering among others. This research investigated the fracture mechanics of reinforced polyester composites on exposure to sudden impact force, using experimental and analytical methods based on impact and Linear Elastic Fracture Mechanics (LEFM) test procedures, to study the stress distribution around crack tip and zone. Plies of randomly varied combination of E-glass fibre in forms of woven roving, hard and soft mat was used as reinforcement in polyester resin matrix to manufacture test specimens. Fourteen (14) test samples with geometry 210 mm x 150 mm were fabricated using hand lay-up method. Hence, were cut and tested in accordance with ASTM standards for composite polymeric material tests under mode I and Charpy impact test conditions, using the compact tension and the Charpy impact test specimens respectively. From the experiment, the fibre volume fraction, the mode I, KI and mode II, KIIstress intensity factors, critical stress, σC,shear stress, τntthe impact energy, E and impact strength, U were determined for each specimen. The mode I fracture toughness, KIC was found to be 4.97 MPa.m1/2 at a critical stress of 13.53MPa while the mode II fracture toughness, KIIC was 1.31 MPa.m1/2 at a shear stress, τntof 3.71MPa and also, the effective thickness was found to be in the range of 80-100mm atfibre volume fraction, Vf of within 0.35-0.50. From the results, the specimens containing woven roving reinforcement were found to possess higher fracture toughness and resistance to both fracture and impact damage. This was largely found to be as a result of fibre bridging and crack arrest mechanisms. This mechanism prevented crack growth direction in specimens containing woven roving not to propagate along the original direction, but change the direction to an inclined path till failure with the exception of those containing soft and hard mat in which the crack grew in the original crack direction as the stress intensity increased. During the impact test, fibre stacking sequence played a vital role, thereby making specimens containing woven roving to resist impact damage and failure, and this resulted in fibre pull-out during fracture. The increase in fibre volume fraction was also found to improve the impact strength of the laminates. From the experiments, ways of improving composite performance were recommended, to ensure optimum impact and fracture resistance.


TABLE OF CONTENTS

Contents Page

Title Page i

Certification ii

Dedication iii

Acknowledgement iv

Abstract v

Table of Contents vi

List of Tables vii

List of Figures viii

Nomenclature ix

CHAPTER ONE INTRODUCTION

1.1 Background of the Study 1

1.2 Why Reinforced Composites are Prone to Impact Damage? 2

1.3 Failure Mechanism in Composite Material Exposed to Sudden Impact Force 4

1.4 Failure Criteria of Composite Materials 5

1.5 Statement of the Problem 7

1.6 Aim and Objectives of the Research 7

1.7 Significance of the Research 8

CHAPTER TWO LITERATURE REVIEW 9

CHAPTER THREE RESEARCH METHODOLOGY

3.1 Materials 13

3.1.1. Reinforced Composite Specimen Manufacture and Preparation 13

3.1.2. Fracture Mechanics Assumptions in Reinforced Composite Analysis 16

3.1.3. Fibre Areal Weight, AW and Volume Fraction Vf Analysis 17

3.2 Test Machines 18

3.2.1 The Universal Testing Machine 18

3.2.2 The Charpy Impact Testing Machine 19

3.3 Description of the Study 19

3.4 Experimental Procedures and Analysis 20

3.4.1 Linear Elastic Fracture Mechanics 20

3.4.2 Test Procedures for the Determination of Mode I Stress Intensity Factor, KI 21

3.4.3 Analysis of Load-Displacement Records and Mathematical Analysis of the SIFs 22

3.4.4 Analysis of Stress Field near the Crack Tip 26

3.5 The Charpy Impact Test 27

3.5.1 Experimental Procedure for Impact Strength Determination 27

3.6 Primary Experimental Data Analysis: Load, P – Displacement, δ diagrams 28

CHAPTER FOUR RESULT AND DISCUSSIONS

Results and Discussions 38

CHAPTER FIVE CONCLUSION AND RECOMMENDATIONS

5.1 Conclusion 63

5.2 Recommendations 65

REFERENCES 67

Fracture Mechanics of Glass Fibre Reinforced Polyester Composites (Gfrp) Subjected to Impact Load
For more Info, call us on
+234 8130 686 500
or
+234 8093 423 853

Share This
  • Type: Project
  • Department: Mechanical Engineering
  • Project ID: MCE0250
  • Access Fee: ₦5,000 ($14)
  • Pages: 85 Pages
  • Format: Microsoft Word
  • Views: 179

500
Leave a comment...

    Related Works

    ABSTRACT Glass mat reinforcement, which can be easily shattered, is widely used across the world in military, automobile, civil, railway and electronic engineering among others. This research investigated the fracture mechanics of reinforced polyester composites on exposure to sudden impact force, using experimental and analytical methods based on... Continue Reading
    ABSTRACT Among various efforts pursued to produce fuel efficient vehicles, light weight engineering (i.e. the use of low-density structurally-efficient materials, the application of advanced manufacturing and joining technologies and the design of highly-integrated, multi-functional components/sub-assemblies) plays a prominent role. In the present... Continue Reading
    Kenaf reinforced polyethylene composites for ballistic protection was produced in this work. The samples of alkaline treated and silane-coupled non-woven matted kenaf fibers were cut to the required dimensions and oriented vertically and horizontally in combinations with a virgin high density polyethylene (VHDPE). The composite panels were... Continue Reading
    Kenaf reinforced polyethylene composites for ballistic protection was produced in this work. The samples of alkaline treated and silane-coupled non-woven matted kenaf fibers were cut to the required dimensions and oriented vertically and horizontally in combinations with a virgin high density polyethylene (VHDPE). The composite panels were... Continue Reading
    Abstract Hydraulic fracturing is an effective well stimulation technique which is introduced in the 1950s and widely used in the oil and gas industry. Most of the works about hydraulic fracture assumed that the fracture is symmetric and either vertical or horizontal. But, several field and laboratory observations show very complex fractures,... Continue Reading
    ABSTRACT Relevant literature for the modeling and analysis of failure of GRP composites were reviewed. Samples of GRP composites were prepared by hand-lay up. Composites samples were subjected to compressive tests using a tensometer. Mechanical characteristics, such as modulus of elasticity; compressive strength, proportionality limit, elastic... Continue Reading
    Abstract Hydraulic fracturing has been an effective technique to stimulate damaged wells or wells producing from low-permeability formation. It has been established that the orientation of a hydraulic fracture is perpendicular to the direction of the least principal stress in the formation. Thus, most pressure transient analysis techniques are... Continue Reading
    Masonry structures are prone to extensive damage followed by failure and collapse when subjected to loads resulting from wind, earthquake and other natural or man-made events. Recent earthquakes and terrorist acts have clearly demonstrated the need for the development of effective and affordable strategies for the strengthening of masonry. As a... Continue Reading
    Masonry structures are prone to extensive damage followed by failure and collapse when subjected to loads resulting from wind, earthquake and other natural or man-made events. Recent earthquakes and terrorist acts have clearly demonstrated the need for the development of effective and affordable strategies for the strengthening of masonry. As a... Continue Reading
    Masonry structures are prone to extensive damage followed by failure and collapse when subjected to loads resulting from wind, earthquake and other natural or man-made events. Recent earthquakes and terrorist acts have clearly demonstrated the need for the development of effective and affordable strategies for the strengthening of masonry. As a... Continue Reading
    Call Us Get this work